Powdr alwmina alffa

Al203
     %

Na2O
     %

SiO2
     %

Fe2O3
     %

Α-Al203
     %

Dwysedd y gwir
g/cm3

Cynradd
Gronynnau
Maint
Μm

Penodol
Arwyneb
Ardal
㎡/g

Yn golygu
Gronynnau
Maint
D50, μm

Roedd Soda isel Calcined α-alwmina, powdr gwreiddiol

IL-10

A5113

≥99.5

0.10

0.03

0.02

95

3.95

1

2.2

IL--20

A6032

≥99.6

0.07

0.03

0.02

96

3.96

3

1.2

IL--40

A7041

≥99.6

0.05

0.03

0.02

97

3.97

4

1.0

Roedd Soda isel Calcined α-alwmina, Micropowder

IL--1G

A5113g1

≥99.3

0.10

0.15

0.02

95

3.95

1

2.6

1.5±0.5

IL--3G

A6032g3

≥99.5

0.07

0.13

0.02

96

3.96

3

1.8

3±0.5

IL--5G

A7042g5

≥99.5

0.05

0.10

0.02

97

3.97

4

1.2

5±0.5

Prif ddiben: plwg spark, swbstrad electronig, tiwbiau trydan gwactod, seramig boby, ac ati.

Roedd Soda cyfrwng Calcined α-alwmina, powdr gwreiddiol

NDM--30

A3224

≥99.5

0.18

0.03

0.02

93

3.93

2

3.5

-

IL-M-40

A5234

≥99.5

0.15

0.03

0.02

95

3.95

3

3.5

-

Roedd Soda cyfrwng Calcined α-alwmina, Micropowder

IL-M-3G

A3224g2

≥99.2

0.18

0.15

0.03

93

3.93

2

3.5

3±0.5

IL-M-4G

A5234g4

≥99.3

0.15

0.15

0.03

95

3.95

3

3.5

4±0.5

Prif ddiben: seramig rholer, pêl seramig alwmina uchel a leinin, Shaped a refractories monolithig ac ati.

Roedd Soda cyffredin Calcined α-alwmina, powdr gwreiddiol

AP 30

A3314

≥99.5

0.28

0.03

0.02

93

3.93

1

3.5

-

AP 40

A5324

≥99.5

0.25

0.03

0.02

95

3.95

2

3.5

-

Roedd Soda cyffredin Calcined α-alwmina, Micropowder

AP-1G

A3314gl

≥99.0

0.28

0.2

0.02

93

3.93

1

3.5

1±0.5

AP-2G

A3314g2

≥99.2

0.28

0.15

0.02

93

3.93

1

3.5

2±0.5

AP-3G

A3314g4

≥99.3

0.25

0.1

0.02

95

3.95

2

3.5

4±0.5

Prif ddiben: deunydd gwrthsafol, mawr a sgleinio, hysbyseb pêl cemegol, ac ati.

Nodyn: yn ogystal â chynhyrchion uchod, ond hefyd y gall wneud RandD a chynhyrchu i ddarparu rhyw fath o gynnyrch yn ôl gofynion y cwsmeriaid.